SabikThermocompNoryl_MX5819Eresin adalah NORYL MX5819E adalah 20% serat karbon diperkuat, tahan api PPO berbasis resin injeksi cetakan.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, pecah, 5 mm/menit | 95 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 8500 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 130 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 7500 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 80°C, aliran | 1.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/120 | 180 | °C | ISO 306 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.18 | g/cm3 | ISO 1183 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL Diakui, Kelas Api 94V-1 (3) | 0.75 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:09/14/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Suhu Peleburan | 290 - 330 | °C |
| Suhu Nozzle | 290 - 310 | °C |
| Suhu depan - Zona 3 | 310 - 330 | °C |
| Tengah - Zona 2 Suhu | 290 - 310 | °C |
| Bagian belakang - Zona 1 Suhu | 270 - 290 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 80 - 120 | °C |
| Sumber GMD, terakhir diperbarui:09/14/2000 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp Noryl_MX5819E.pdf |
|