SabikThermocompDF0029ERresin adalahsenyawa berbasis resin polikarbonat yang mengandung Serat Kaca.
termasuk: Mudah Molding, Release Mold, Flame Retardant
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 83 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 79 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 3.9 | % | ASTM D 638 |
| Tekanan tarik, putus | 5.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 4130 | MPa | ASTM D 638 |
| Modulus Flexural | 4130 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 84 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 81 | MPa | ISO 527 |
| Tekanan tarik, hasil | 3.7 | % | ISO 527 |
| Tekanan tarik, putus | 4.7 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 4460 | MPa | ISO 527 |
| Tekanan Flexural | 129 | MPa | ISO 178 |
| Modulus Flexural | 4100 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 865 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 85 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 16 | J | ASTM D 3763 |
| Dampak Multiaxial | 7 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 59 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 142 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 2 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 5.04E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.94E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 5.9E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 143 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 136 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.3 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.1 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.6 - 0.8 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.6 - 0.8 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.67 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.68 | % | ISO 294 |
| Kepadatan | 1.3 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 305 - 325 | °C |
| Suhu depan - Zona 3 | 320 - 330 | °C |
| Tengah - Zona 2 Suhu | 310 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 295 - 305 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |