SabikThermocompNoryl_FM4025resin adalah GR/MR 40%, busa struktural modulus tinggi. 10% penurunan berat badan, ketebalan dinding 0,250 "
| Mekanis | Nilai | Satuan | Standar |
| busa - MEKANIS 6.4 mm Wt Pengurangan | 10 | % | - |
| Tekanan tarik, hasil, 6,35 mm | 82 | MPa | ASTM D 638 |
| Tekanan tarik, hasil, 6,35 mm | 1.5 | % | ASTM D 638 |
| Tekanan lentur, hasil, 6,4 mm | 121 | MPa | ASTM D 790 |
| Flexural Modulus, 6,4 mm | 7920 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 85 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 100 | mg/1000cy | ASTM D 1044 |
| Koefisien gesekan pada diri sendiri, statis | 0.55 | - | ASTM D 1894 |
| Koefisien gesekan pada baja, statis | 0.52 | - | ASTM D 1894 |
| Dampak | Nilai | Satuan | Standar |
| BUMEN - Dampak 6.4 mm Wt Pengurangan | 10 | % | - |
| Izod Dampak, bertanduk, 23°C, 6,4mm | 69 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| BUMEN - PEMERINTAH 6.4mm Wt Pengurangan | 10 | % | - |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 118 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 110 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 2.34E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, xflow | 3.42E-05 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 50 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| busa - PHYSICAL 6.4mm Wt Pengurangan | 10 | % | - |
| Pengurangan Berat Badan | 10 | % | Metode S-Plastics |
| Gravitasi Spesifik | 1.43 | - | ASTM D 792 |
| Gravitasi spesifik, cetakan busa | 1.29 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.08 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 6,4 mm | 0.15 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 6,4 mm | 0.25 | % | Metode S-Plastics |
| Rasio Poisson | 0.3 | - | ASTM D 638 |
| Listrik | Nilai | Satuan | Standar |
| busa - Listrik 6.4 mm Wt Pengurangan | 20 | % | - |
| Resistivitas Volume | 1.E+17 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.E+17 | Ohm | ASTM D 257 |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 0 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 4 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 4 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 4 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| FOAM - Kelas Api Kepadatan Minimal | 1.26 | g/cm3 | - |
| UL Diakui, Kelas Api 94V-1 (3) | 2.89 | mm | UL 94 |
| UL diakui, 94V-0 Flame Class Rating (3) | 5 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 2.89 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:04/08/1993 | |||
| Parameter | ||
| Membentuk busa struktural | Nilai | Satuan |
| Agen Blowing, Sistem Fisik | Gas nitrogen | - |
| Agen Blowing, Sistem Kimia | FNC30X | - |
| Jangkauan konsentrasi (Agen Blowing) | 1 - 3 | % |
| Konsentrasi yang Disarankan (Agen Blowing) | 2 | % |
| Suhu pengeringan (resin) | 105 - 110 | °C |
| Waktu pengeringan (resin) | 2 - 4 | jam |
| Waktu pengeringan (resin, kumulatif) | 8 | jam |
| Suhu Peleburan | 270 - 310 | °C |
| Suhu Nozzle | 270 - 305 | °C |
| Suhu Depan | 270 - 305 | °C |
| Suhu Rata-rata | 270 - 305 | °C |
| Suhu Belakang | 260 - 290 | °C |
| Suhu Cetakan | 65 - 80 | °C |
| Sumber GMD, terakhir diperbarui:04/08/1993 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp Noryl_FM4025.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|