SabikThermocompC1000XXPresin adalahKomposisi yang didasarkan pada resin Polystyrene.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 50 mm/menit | 23 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 1.9 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1400 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 49 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2100 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 60 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 81 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran | 0.5 | % | Metode S-Plastics |
| Kepadatan | 1.04 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:01/16/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 250 | °C |
| Suhu depan - Zona 3 | 265 - 275 | °C |
| Tengah - Zona 2 Suhu | 245 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 230 | °C |
| Suhu Cetakan | 40 - 65 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:01/16/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp C1000XXP.pdf |
|