SabikThermocompHSG-P-1100A EXPresin adalah senyawa berdasarkan resin Nylon 6.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 40 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 15490 | MPa | ASTM D 638 |
| Tekanan Flexural | 85 | MPa | ASTM D 790 |
| Modulus Flexural | 16400 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 251 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 66 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 152 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 11 | g/cm3 | ASTM D 792 |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 265 - 270 | °C |
| Suhu depan - Zona 3 | 260 - 270 | °C |
| Tengah - Zona 2 Suhu | 250 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 250 | °C |
| Suhu Cetakan | 80 - 95 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp HSG-P-1100A EXP.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|