SabikThermocompZX06323resin adalah Bahan ini adalah mineral diisi PPO kelas dengan konstanta dielektrik tinggi dan tangen kehilangan rendah
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 54 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 4.2 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/menit | 4140 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 102 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 102 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3940 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 0 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 54 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 0 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 4.7 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 4080 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/menit | 4390 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 294 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 46 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 20 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 122 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 122 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.95 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.1 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.64 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.56 | % | ASTM D 955 |
| Kepadatan | 1.95 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 300°C/5,0 kg | 8 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Faktor Dissipasi, 900MHz | 0.003 | - | ASTM D 150 |
| Permittivitas relatif, 900MHz | 6.4 | - | ASTM D 2520 - Mth B |
| Sumber GMD, terakhir diperbarui:2007/06/28 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 105 | °C |
| Waktu Pengeringan | 3 - 5 | jam |
| Suhu Peleburan | 295 - 305 | °C |
| Suhu Nozzle | 290 - 295 | °C |
| Suhu depan - Zona 3 | 300 - 305 | °C |
| Tengah - Zona 2 Suhu | 290 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 280 - 285 | °C |
| Suhu Cetakan | 90 | °C |
| Tekanan Belakang | 9 | MPa |
| Kecepatan sekrup | 100 | rpm |
| Sumber GMD, terakhir diperbarui:2007/06/28 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp ZX06323.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|