SabikThermocompZF406XXXresin adalah senyawa yang didasarkan pada resin PPO Blend yang mengandung Serat Kaca, Retardant Flame.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 95 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 0.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 11530 | MPa | ASTM D 638 |
| Tekanan Flexural | 199 | MPa | ASTM D 790 |
| Modulus Flexural | 11450 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 119 | MPa | ISO 527 |
| Tekanan tarik, putus | 1.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 11690 | MPa | ISO 527 |
| Tekanan Flexural | 192 | MPa | ISO 178 |
| Modulus Flexural | 9900 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 523 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 80 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 29 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 263 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.98E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.76E-05 | 1/°C | ASTM E 831 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 262 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.54 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.1 - 0.3 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.5 - 0.7 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.1 - 0.3 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.5 - 0.7 | % | ISO 294 |
| Kepadatan | 1.53 | g/cm3 | ISO 1183 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 1.55 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:12/17/2004 | |||