SabikThermocompRF008ESYresinadalah senyawa yang didasarkan pada resin Nylon 66 yang mengandung Serat Kaca.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 168 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 2.4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 13030 | MPa | ASTM D 638 |
| Tekanan Flexural | 246 | MPa | ASTM D 790 |
| Modulus Flexural | 9100 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 168 | MPa | ISO 527 |
| Tekanan tarik, putus | 2.8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 11900 | MPa | ISO 527 |
| Tekanan Flexural | 263 | MPa | ISO 178 |
| Modulus Flexural | 11300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1089 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 112 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 11 | J | ASTM D 3763 |
| Dampak Multiaxial | 3 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 74 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 12 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 251 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 229 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 227 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.471 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.77 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.2 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1.1 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.17 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 1.05 | % | ISO 294 |
| Kepadatan | 1.46 | g/cm3 | ISO 1183 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94HB (3) | 1.5 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:10/02/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 280 - 305 | °C |
| Suhu depan - Zona 3 | 295 - 305 | °C |
| Tengah - Zona 2 Suhu | 280 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 265 - 275 | °C |
| Suhu Cetakan | 95 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/02/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp RF008ESY.pdf |
|