SabikThermocompZF008resin adalah senyawa berdasarkan PPO yang dimodifikasi yang mengandung Serat Kaca.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 98 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 0.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 18510 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 196 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 22590 | MPa | ASTM D 790 |
| Tekanan tarik, pecah, 5 mm/menit | 93 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.1 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 13330 | MPa | ISO 527 |
| Tekanan Flexural | 325 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 21370 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 428 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 96 | J/m | ASTM D 256 |
| Dampak Multiaxial | 2 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 11 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 26 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 138 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 132 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 4.2E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 4.6E-05 | 1/°C | ASTM D 696 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 138 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 133 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.38 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.07 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.2 - 0.4 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.5 - 0.7 | % | ASTM D 955 |
| Kepadatan | 1.38 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:2009/01/13 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 300 - 305 | °C |
| Suhu depan - Zona 3 | 300 - 310 | °C |
| Tengah - Zona 2 Suhu | 290 - 300 | °C |
| Bagian belakang - Zona 1 Suhu | 275 - 290 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:2009/01/13 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp ZF008.pdf |
|