SabikThermocompZF006resin adalah senyawa berdasarkan PPE+PS Blend resin yang mengandung Serat Kaca.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 108 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 9870 | MPa | ASTM D 638 |
| Tekanan Flexural | 165 | MPa | ASTM D 790 |
| Modulus Flexural | 8900 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 528 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 117 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 135 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.31 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.3 | % | ASTM D 955 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 300 - 305 | °C |
| Suhu depan - Zona 3 | 300 - 310 | °C |
| Tengah - Zona 2 Suhu | 290 - 300 | °C |
| Bagian belakang - Zona 1 Suhu | 275 - 290 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp ZF006.pdf |
|