SabikThermocompYF003Sresin adalah senyawa berbasis poliester elastomer yang mengandung Serat Kaca.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 50 mm/menit | 43 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 42 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 15 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1500 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 45 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 85 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 28 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 60°C, aliran | 3.4E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 1.95E-04 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 163 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 121 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran | 0.5 | % | Metode S-Plastics |
| Kepadatan | 1.3 | g/cm3 | ISO 1183 |
| Penyerapan air, 23°C/24 jam | 0.54 | % | ISO 62-1 |
| Sumber GMD, terakhir diperbarui:12/09/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.1 | % |
| Suhu Peleburan | 215 - 240 | °C |
| Suhu depan - Zona 3 | 225 - 240 | °C |
| Tengah - Zona 2 Suhu | 205 - 215 | °C |
| Bagian belakang - Zona 1 Suhu | 180 - 195 | °C |
| Suhu Cetakan | 25 - 55 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:12/09/2008 | ||