SabikThermocompXF006Sresin adalah senyawa yang didasarkan pada Nylon Amorf yang mengandung Serat Kaca.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 138 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 9650 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 209 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 208 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 9060 | MPa | ASTM D 790 |
| Tekanan tarik, pecah, 5 mm/menit | 141 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 9020 | MPa | ISO 527 |
| Tekanan Flexural | 214 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 8910 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 632 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 56 | J/m | ASTM D 256 |
| Dampak Multiaxial | 3 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 11 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 38 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 142 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 138 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 4.4E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 3.5E-05 | 1/°C | ASTM D 696 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 144 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 137 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.36 | - | ASTM D 792 |
| Kepadatan | 1.36 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.22 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam (5) | 0 - 0 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam (5) | 0.2 - 0.4 | % | ASTM D 955 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.28 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:2010/07/08 | |||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp XF006S.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|