SabikThermocompAX08306resin adalahsenyawa yang didasarkan pada resin Acrylonitrile Butadiene Styrene yang mengandung Mineral.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 37 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 35 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 37 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 34 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 1.8 | % | ASTM D 638 |
| Tekanan tarik, putus | 6 | % | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 1.8 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 6.9 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/menit | 3180 | MPa | ASTM D 638 |
| Tekanan Flexural | 68 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 92 | MPa | ASTM D 790 |
| Modulus Flexural | 3270 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3060 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 36 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 33 | MPa | ISO 527 |
| Tekanan tarik, putus | 7.5 | % | ISO 527 |
| Tekanan Flexural | 64 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 64.1 | % | ISO 178 |
| Modulus Flexural | 3010 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 288 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 26 | J/m | ASTM D 256 |
| Izod Impact, bernotas 80*10*3 +23°C | 3 | kJ/m2 | ISO 180/1A |
| Izod Impact, tidak diukir 80*10*4 +23°C | 22 | kJ/m2 | ISO 180/1U |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 86 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 87 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.17 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.22 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.5 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.6 | % | ASTM D 955 |
| Kepadatan | 1.17 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.32 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Permittivitas relatif, 1 GHz | 2.75 | - | ASTM D 150 |
| Faktor Dissipasi, 1 GHz | 0.0024 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:08/20/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 - 0.1 | % |
| Suhu Peleburan | 260 | °C |
| Suhu depan - Zona 3 | 265 - 275 | °C |
| Tengah - Zona 2 Suhu | 230 - 245 | °C |
| Bagian belakang - Zona 1 Suhu | 205 - 215 | °C |
| Suhu Cetakan | 70 - 80 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:08/20/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |