SabikThermocompWZ002resin adalah senyawa yang didasarkan pada resin Polybutylene Terephalate yang mengandung Milled Glass.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 47 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2.3 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 5000 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2900 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 20 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 3 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 149 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 64 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran | 1.9 | % | Metode S-Plastics |
| Kepadatan | 1.4 | g/cm3 | ISO 1183 |
| Penyerapan air, 23°C/24 jam | 0.1 | % | ISO 62-1 |
| Sumber GMD, terakhir diperbarui:12/31/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 240 - 265 | °C |
| Suhu depan - Zona 3 | 260 - 270 | °C |
| Tengah - Zona 2 Suhu | 245 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 230 | °C |
| Suhu Cetakan | 80 - 100 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:12/31/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
Untuk informasi lebih lanjut silahkan download lembar data | |
 | S-Plastics Thermocomp WZ002.pdf |