SabikThermocompDF006Presin adalahsenyawa berbasis resin polikarbonat yang mengandung Serat Kaca.
termasuk: Pengolahan Luar Biasa.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 124 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 124 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 124 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 2.4 | % | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2.4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2.4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 10480 | MPa | ASTM D 638 |
| Tekanan Flexural | 193 | MPa | ASTM D 790 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 165 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 165 | MPa | ASTM D 790 |
| Modulus Flexural | 8480 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 8720 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 125 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 125 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 125 | MPa | ISO 527 |
| Tekanan tarik, putus | 2.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 10010 | MPa | ISO 527 |
| Tekanan Flexural | 193 | MPa | ISO 178 |
| Modulus Flexural | 8740 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 774 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 112 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 13 | J | ASTM D 3763 |
| Dampak Multiaxial | 2 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 47 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 134 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 131 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 134 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.424 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.1 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.15 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.67 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.09 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.51 | % | ISO 294 |
| Kepadatan | 1.42 | g/cm3 | ISO 1183 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-2 (3) | 1.5 | mm | UL 94 oleh GE |
| Sesuai UL, Kelas Api 94V-0 (3) | 3 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:09/27/2004 | |||
| Pencetakan Injeksi | Nilai | Satuan | |
| Suhu Pengeringan | 120 | °C | |
| Waktu Pengeringan | 4 | jam | |
| Kandungan Kelembaban Maksimal | 0.02 | % | |
| Suhu Peleburan | 305 - 325 | °C | |
| Suhu depan - Zona 3 | 320 - 330 | °C | |
| Tengah - Zona 2 Suhu | 310 - 320 | °C | |
| Bagian belakang - Zona 1 Suhu | 295 - 305 | °C | |
| Suhu Cetakan | 80 - 110 | °C | |
| Tekanan Belakang | 0.2 - 0.3 | MPa | |
| Kecepatan sekrup | 30 - 60 | rpm | |
| Sumber GMD, terakhir diperbarui:09/27/2004 | |||
| Nilai properti ini tidak dimaksudkan untuk tujuan spesifikasi. | |||
| Silakan periksa dengan (kantor penjualan lokal) untuk ketersediaan di wilayah Anda | |||
| (1) Hanya nilai-nilai tipikal. variasi dalam toleransi normal mungkin untuk berbagai warna. semua nilai diukur setelah setidaknya 48 jam Semua sifat, kecuali volume leleh dan aliran leleh diukur pada mesin injeksi Semua sampel yang diuji menurut standar uji ISO disiapkan sesuai dengan ISO 294. |
|||
| (2) Hanya data tipikal untuk tujuan seleksi. | |||
| (3) Klasifikasi ini tidak dimaksudkan untuk mencerminkan bahaya yang ditimbulkan oleh bahan ini atau bahan lain dalam kondisi kebakaran yang sebenarnya. | |||
| (4) Pengukuran internal menurut standar UL. | |||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp DF006P.pdf |
|