SabikTermokompAF006XXZresin adalahsenyawa berbahan dasar resin Acrylonitrile Butadiene Styrene yang mengandung Fiber Glass.
| SIFAT KHUSUS (1) | |||
| MEKANIS | Nilai | Satuan | Standar |
| Stres Tarik, putus | 96 | MPa | ASTM D 638 |
| Regangan Tarik, putus | 1.8 | % | ASTM D 638 |
| Stres Lentur | 153 | MPa | ASTM D 790 |
| Modulus Lentur | 9170 | MPa | ASTM D 790 |
| Stres Tarik, putus | 83 | MPa | ISO 527 |
| Regangan Tarik, pecahkan | 1.7 | % | ISO 527 |
| Stres Lentur | 119 | MPa | ISO 178 |
| Modulus Lentur | 8000 | MPa | ISO 178 |
| DAMPAK | Nilai | Satuan | Standar |
| Izod Impact, tak berlekuk, 23°C | 283 | J/m | ASTM D 4812 |
| Izod Impact, berlekuk, 23°C | 58 | J/m | ASTM D 256 |
| Izod Impact, berlekuk 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PANAS | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak dianil | 102 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Datar 80*10*4 sp=64mm | 102 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.28 | gram/cm³ | ASTM D 792 |
| Penyusutan Cetakan, aliran, 24 jam | 0,2 | % | ASTM D 955 |
| Penyusutan Cetakan, xflow, 24 jam | 0,4 | % | ASTM D 955 |
| Sumber GMD, terakhir diperbarui: 10/01/2004 | |||
| Parameter | ||
| Cetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kadar Air Maksimum | 0,05 - 0,1 | % |
| Suhu Leleh | 260 | °C |
| Depan - Suhu Zona 3 | 265 - 275 | °C |
| Suhu Tengah - Zona 2 | 230 - 245 | °C |
| Belakang - Suhu Zona 1 | 205 - 215 | °C |
| Suhu Cetakan | 70 - 80 | °C |
| Tekanan balik | 0,2 - 0,3 | MPa |
| Kecepatan Sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui: 10/01/2004 | ||