SabikThermocompRF006SXSresin adalahPemanasan stabil, 30% serat kaca diperkuat Polyamide 66 resin injeksi.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, pecah, 5 mm/menit | 170 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 9400 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 260 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 9000 | MPa | ISO 178 |
| Kekerasan, Rockwell L | 113 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -20°C | 9 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 8 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -40°C | 8 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | 75 | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 55 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Konduktivitas Termal | 0.33 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 60°C, aliran | 2.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 7.5E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 260 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 258 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 260 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 248 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 65 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 65 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 65 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.2 - 0.4 | % | Metode S-Plastics |
| Kepadatan | 1.37 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 4.5 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 1.2 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+16 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+16 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 19 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 3.4 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 3.2 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.0068 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.015 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 500 | V | IEC 60112 |
| Indeks Pelacakan Perbandingan, M | 400 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 0.75 | mm | UL 94 |
| UL Diakui, 94HB Kelas Api Nilai ke-2 (3) | 3 | mm | UL 94 |
| Glow Wire Flammability Index 650°C, melewati pada | 2 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 25 | % | ISO 4589 |
| Kecepatan pembakaran FMVSS, ketebalan 2 mm | 6 | mm/menit | FMVSS 302 |
| Kecepatan pembakaran FMVSS, ketebalan 3 mm | 2 | mm/menit | FMVSS 302 |
| Sumber GMD, terakhir diperbarui:11/04/2003 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 75 - 85 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.2 | % |
| Suhu Peleburan | 260 - 290 | °C |
| Suhu Nozzle | 250 - 270 | °C |
| Suhu depan - Zona 3 | 260 - 280 | °C |
| Tengah - Zona 2 Suhu | 260 - 280 | °C |
| Bagian belakang - Zona 1 Suhu | 270 - 290 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 70 - 120 | °C |
| Sumber GMD, terakhir diperbarui:11/04/2003 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp RF006SXS.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|