SabikThermocompWX06438resin adalah senyawa yang didasarkan pada polybutylene terephalat resin yang mengandung Serat Kaca.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 120 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 120 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 2.3 | % | ASTM D 638 |
| Tekanan tarik, putus | 2.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 10020 | MPa | ASTM D 638 |
| Tekanan Flexural | 172 | MPa | ASTM D 790 |
| Modulus Flexural | 8790 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 119 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 119 | MPa | ISO 527 |
| Tekanan tarik, hasil | 2.1 | % | ISO 527 |
| Tekanan tarik, putus | 2.1 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 9520 | MPa | ISO 527 |
| Tekanan Flexural | 162 | MPa | ISO 178 |
| Modulus Flexural | 8180 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 660 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 74 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 13 | J | ASTM D 3763 |
| Dampak Multiaxial | 2 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 206 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 203 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.52 | g/cm3 | ASTM D 792 |
| Sumber GMD, terakhir diperbarui:02/27/2007 | |||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp WX06438.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|