SabikThermocompWFB44resin adalah senyawa yang didasarkan pada resin Polybutylene Terephalate yang mengandung Serat Kaca, Manik Kaca.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, pecah, 5 mm/menit | 100 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 8000 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 157 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 140 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 7200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 35 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 60°C, aliran | 3.9E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 9.9E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 219 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 192 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.2 - 0.5 | % | Metode S-Plastics |
| Kepadatan | 1.62 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+14 | Ohm | ASTM D 257 |
| Indeks Pelacakan Perbandingan | 325 | V | IEC 60112 |
| Sumber GMD, terakhir diperbarui:02/26/2007 | |||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp WFB44.pdf |
|