SabikThermocompWF0039Uresin adalah senyawa yang didasarkan pada resin Thermoplastic Polyester (PBT) yang mengandung Serat Kaca.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 95 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 7240 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 137 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 6060 | MPa | ASTM D 790 |
| Tekanan tarik, pecah, 5 mm/menit | 95 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 7080 | MPa | ISO 527 |
| Tekanan Flexural | 145 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 6360 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 342 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 48 | J/m | ASTM D 256 |
| Dampak Multiaxial | 1 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 4 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 19 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 215 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 194 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 4.23E+01 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 1.07E+02 | 1/°C | ASTM D 696 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 212 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 185 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.58 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.05 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam (5) | 0.5 - 0.7 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam (5) | 1 - 3 | % | ASTM D 955 |
| Kepadatan | 1.57 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:2009/06/10 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 245 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 260 | °C |
| Tengah - Zona 2 Suhu | 245 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 245 | °C |
| Suhu Cetakan | 80 - 100 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:2009/06/10 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp WF0039U.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|