SabikThermocompRF0069Fresin adalahApi tahan, 30% serat kaca diperkuat Polyamide 66 resin injeksi cetakan.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, pecah, 5 mm/menit | 165 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 9500 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 190 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 9300 | MPa | ISO 178 |
| Kekerasan, Rockwell L | 108 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -20°C | 7 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | 60 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 60°C, aliran | 2.3E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/120 | 258 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 262 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 248 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 65 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 65 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 65 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.2 - 0.3 | % | Metode S-Plastics |
| Kepadatan | 1.58 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 4 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Indeks Pelacakan Perbandingan | 375 | V | IEC 60112 |
| Indeks Pelacakan Perbandingan, M | 275 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.75 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 2 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 31 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:11/05/2003 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 75 - 85 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.2 | % |
| Suhu Peleburan | 260 - 280 | °C |
| Suhu Nozzle | 250 - 270 | °C |
| Suhu depan - Zona 3 | 260 - 280 | °C |
| Tengah - Zona 2 Suhu | 260 - 280 | °C |
| Bagian belakang - Zona 1 Suhu | 270 - 290 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 70 - 100 | °C |
| Sumber GMD, terakhir diperbarui:11/05/2003 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp RF0069F.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|