SabikThermocompRF0067Kresinadalah senyawa berbasis resin Nylon 66 yang mengandung Serat Kaca, Flame Retardant.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, pecah, 5 mm/menit | 110 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.8 | % | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 141 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 8200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 30 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 197 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) (5) | 0.2 - 0.4 | % | Metode S-Plastics |
| Kepadatan | 1.45 | g/cm3 | ISO 1183 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.8 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 1.5 | mm | IEC 60695-2-12 |
| Sumber GMD, terakhir diperbarui:2006/12/13 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.2 | % |
| Suhu Peleburan | 270 - 290 | °C |
| Suhu depan - Zona 3 | 280 - 290 | °C |
| Tengah - Zona 2 Suhu | 265 - 285 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 280 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Tekanan Belakang | >1 | MPa |
| Kecepatan sekrup | 80 - 120 | rpm |
| Sumber GMD, terakhir diperbarui:2006/12/13 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp RF0067K.pdf |
|