SabikThermocomp9X07435Xresin adalah...
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 60 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 59 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 1.8 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 5450 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 95 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 95 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 5350 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 51 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 51 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 1.5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 4810 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 93 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 2.2 | % | ISO 178 |
| Flexural Modulus, 2 mm/menit | 5010 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 272 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 35 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 18 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 3 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 101 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 110 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.25 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.09 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.9 - 1.1 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1.1 - 1.3 | % | ASTM D 955 |
| Listrik | Nilai | Satuan | Standar |
| Permittivitas relatif, 1 GHz | 2.9 | - | ASTM D 150 |
| Faktor Dissipasi, 1 GHz | 0.0046 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:02/07/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 95 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 300 - 310 | °C |
| Suhu Nozzle | 300 - 310 | °C |
| Suhu depan - Zona 3 | 300 - 310 | °C |
| Tengah - Zona 2 Suhu | 300 - 310 | °C |
| Bagian belakang - Zona 1 Suhu | 300 - 310 | °C |
| Suhu Cetakan | 105 - 120 | °C |
| Tekanan Belakang | 50 - 100 | MPa |
| Sumber GMD, terakhir diperbarui:02/07/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp 9X07435X.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|