SabikThermocompUX08325resin adalah...
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 135 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 10880 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 197 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 194 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 9770 | MPa | ASTM D 790 |
| Tekanan tarik, pecah, 5 mm/menit | 125 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.6 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 11080 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 194 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 2 | % | ISO 178 |
| Flexural Modulus, 2 mm/menit | 9610 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 351 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 31 | J/m | ASTM D 256 |
| Izod Impact, bernotas 80*10*4 +23°C | 2 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 263 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.21E+01 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.43E+01 | 1/°C | ASTM E 831 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 261 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.55 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran (5) | 0.41 | % | Metode S-Plastics |
| Penyusutan jamur, xflow (5) | 0.52 | % | Metode S-Plastics |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.53 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:2009/08/12 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 | % |
| Suhu Peleburan | 315 - 330 | °C |
| Suhu depan - Zona 3 | 325 - 340 | °C |
| Tengah - Zona 2 Suhu | 315 - 325 | °C |
| Bagian belakang - Zona 1 Suhu | 310 - 320 | °C |
| Suhu Cetakan | 140 - 165 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:2009/08/12 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp UX08325.pdf |
|