SabikThermocompRF002SXSresinadalah resin dasar Nylon 6/6 yang mengandung serat kaca.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 95 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 5440 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 144 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 147 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 4340 | MPa | ASTM D 790 |
| Tekanan tarik, pecah, 5 mm/menit | 87 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 5430 | MPa | ISO 527 |
| Tekanan Flexural | 135 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 4480 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 285 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 30 | J/m | ASTM D 256 |
| Dampak Multiaxial | 1 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 5 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 21 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 3 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 256 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 238 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 4.1E+01 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 8.2E+01 | 1/°C | ASTM D 696 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 252 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 221 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.22 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.86 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam (5) | 0.9 - 2 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam (5) | 1 - 3 | % | ASTM D 955 |
| Kepadatan | 1.22 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 1.2 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:2009/06/09 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 280 - 305 | °C |
| Suhu depan - Zona 3 | 295 - 305 | °C |
| Tengah - Zona 2 Suhu | 280 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 265 - 275 | °C |
| Suhu Cetakan | 95 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:2009/06/09 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |