SabikThermocompRF0029Sresinadalah senyawa yang didasarkan pada resin Nylon 66 yang mengandung Serat Kaca, Retardant Flame.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 101 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 101 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 2.5 | % | ASTM D 638 |
| Tekanan tarik, putus | 2.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 6890 | MPa | ASTM D 638 |
| Tekanan Flexural | 151 | MPa | ASTM D 790 |
| Modulus Flexural | 5510 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 102 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 102 | MPa | ISO 527 |
| Tekanan tarik, hasil | 2.4 | % | ISO 527 |
| Tekanan tarik, putus | 2.4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 6370 | MPa | ISO 527 |
| Tekanan Flexural | 150 | MPa | ISO 178 |
| Modulus Flexural | 5900 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 501 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 42 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 8 | J | ASTM D 3763 |
| Dampak Multiaxial | 1 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 33 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 252 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 233 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.56E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 4.32E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 7.6E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 4.2E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 249 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 219 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.48 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.5 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.9 - 1.1 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1.2 - 1.4 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.98 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 1.3 | % | ISO 294 |
| Kepadatan | 1.48 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 275 - 290 | °C |
| Suhu depan - Zona 3 | 295 - 305 | °C |
| Tengah - Zona 2 Suhu | 280 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 265 - 275 | °C |
| Suhu Cetakan | 80 - 95 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp RF0029S.pdf |
|