SabikThermocomp9X07430resin adalahPBT+PC Alloy, Kaca dan Mineral Dipenuhi, Tidak Transparan, Tahan Cuaca
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 57 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 51 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2.9 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 4.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 3300 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 99 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3140 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 56 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 3.1 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 4.9 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3160 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 97 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3020 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 715 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 80 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 9 | J | ASTM D 3763 |
| Dampak Multiaxial | 7 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 14 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 47 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 102 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 5.7E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 8.3E-05 | 1/°C | ASTM E 831 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 105 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.31 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.11 | % | ASTM D 570 |
| Penyusutan jamur, aliran | 0.51 | % | Metode S-Plastics |
| Penyusutan jamur, aliran | 0.59 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 24 jam | 0.5 - 0.51 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.58 - 0.59 | % | ASTM D 955 |
| Kepadatan | 1.31 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.16 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:2009/01/29 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 - 110 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 260 - 280 | °C |
| Suhu Nozzle | 260 - 280 | °C |
| Suhu depan - Zona 3 | 260 - 280 | °C |
| Tengah - Zona 2 Suhu | 255 - 275 | °C |
| Bagian belakang - Zona 1 Suhu | 245 - 270 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Sumber GMD, terakhir diperbarui:2009/01/29 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp 9X07430.pdf |
|