SabikThermocomp9X02841resin adalahadalah campuran PBT/polikarbonat yang mengandung pengisi khusus.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 83 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 83 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2.7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 5120 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 127 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 123 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 4600 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 80 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 80 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2.6 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.6 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 4880 | MPa | ISO 527 |
| Tekanan Flexural | 115 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 4480 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 522 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 78 | J/m | ASTM D 256 |
| Dampak Multiaxial | 4 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 16 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 31 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 141 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 115 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 4.1E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 6.3E-05 | 1/°C | ASTM D 696 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 140 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 115 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.33 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.09 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.4 - 0.6 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.6 - 0.8 | % | ASTM D 955 |
| Kepadatan | 1.33 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.14 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:11/21/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 240 - 265 | °C |
| Suhu depan - Zona 3 | 260 - 270 | °C |
| Tengah - Zona 2 Suhu | 245 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 230 | °C |
| Suhu Cetakan | 80 - 100 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:11/21/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp 9X02841.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|