SabikThermocompRC006Hresinadalah senyawa yang didasarkan pada resin Nylon 66 yang mengandung Serat Karbon.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 266 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 27780 | MPa | ASTM D 638 |
| Tekanan Flexural | 408 | MPa | ASTM D 790 |
| Modulus Flexural | 18750 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 271 | MPa | ISO 527 |
| Tekanan tarik, putus | 1.9 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 22650 | MPa | ISO 527 |
| Tekanan Flexural | 411 | MPa | ISO 178 |
| Modulus Flexural | 21020 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1014 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 96 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 14 | J | ASTM D 3763 |
| Dampak Multiaxial | 3 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 68 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 11 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 261 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.08E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 4.86E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 1.15E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 4.86E-05 | 1/°C | ISO 11359-2 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.278 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.65 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.1 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.6 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.08 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.56 | % | ISO 294 |
| Pakai faktor pencuci | 20 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Dimodifikasi |
| COF Dinamis | 0.46 | - | ASTM D 3702 Dimodifikasi |
| COF statis | 0.36 | - | ASTM D 3702 Dimodifikasi |
| Kepadatan | 1.27 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 1.14 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:10/02/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 280 - 305 | °C |
| Suhu depan - Zona 3 | 295 - 305 | °C |
| Tengah - Zona 2 Suhu | 280 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 265 - 275 | °C |
| Suhu Cetakan | 95 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/02/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp RC006H.pdf |
|