SabikThermocomp2X95787resin adalahsenyawa yang didasarkan pada resin Etilena Tetrafluoroethylene Copolymer yang mengandung Serat Karbon.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 48 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 45 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 9.3 | % | ASTM D 638 |
| Tekanan tarik, putus | 13.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 42740 | MPa | ASTM D 638 |
| Modulus Flexural | 33780 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 47 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 45 | MPa | ISO 527 |
| Tekanan tarik, hasil | 8.6 | % | ISO 527 |
| Tekanan tarik, putus | 12.8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 4050 | MPa | ISO 527 |
| Tekanan Flexural | 66 | MPa | ISO 178 |
| Modulus Flexural | 4000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1335 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 480 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 19 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 83 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 24 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 222 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 107 | °C | ASTM D 648 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 203 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 91 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.84 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 1.8 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 2.4 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 1.8 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 2.4 | % | ISO 294 |
| Kepadatan | 1.83 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 370 - 390 | °C |
| Suhu depan - Zona 3 | 390 - 400 | °C |
| Tengah - Zona 2 Suhu | 355 - 365 | °C |
| Bagian belakang - Zona 1 Suhu | 315 - 325 | °C |
| Suhu Cetakan | 140 - 165 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp 2X95787.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|