SabikThermocomp2X04505resin adalahadalah senyawa yang didasarkan pada resin Etilena Tetrafluoroethylene Copolymer yang mengandung Serat Karbon.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 87 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 85 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 4.5 | % | ASTM D 638 |
| Tekanan tarik, putus | 4.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 15160 | MPa | ASTM D 638 |
| Modulus Flexural | 10340 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 89 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 88 | MPa | ISO 527 |
| Tekanan tarik, hasil | 4.6 | % | ISO 527 |
| Tekanan tarik, putus | 4.9 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 11580 | MPa | ISO 527 |
| Tekanan Flexural | 319 | MPa | ISO 178 |
| Modulus Flexural | 18800 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1030 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 272 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 18 | J | ASTM D 3763 |
| Dampak Multiaxial | 8 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 58 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 23 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 255 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 222 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.74E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.26E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 7.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.2E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 251 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 207 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.75 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | Satu, satu.2 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1.8 - 2 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 1.1 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 1.9 | % | ISO 294 |
| Kepadatan | 1.74 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 315 | °C |
| Suhu depan - Zona 3 | 330 - 345 | °C |
| Tengah - Zona 2 Suhu | 310 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 280 - 295 | °C |
| Suhu Cetakan | 95 - 120 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |