SabikThermocomp2X03624Hresin adalahsenyawa yang didasarkan pada resin FEP yang mengandung Mineral.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 13 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | NB | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 9.3 | % | ASTM D 638 |
| Tekanan tarik, putus | NB | % | ASTM D 638 |
| Tekanan Flexural | 13 | MPa | ASTM D 790 |
| Modulus Flexural | 620 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 14 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | NB | MPa | ISO 527 |
| Tekanan tarik, hasil | 7.2 | % | ISO 527 |
| Tekanan tarik, putus | NB | % | ISO 527 |
| Tekanan Flexural | 16 | MPa | ISO 178 |
| Modulus Flexural | 600 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | NB | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 566 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 30 | J | ASTM D 3763 |
| Dampak Multiaxial | 46 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 64 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 53 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.21E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.26E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 1.21E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.28E-04 | 1/°C | ISO 11359-2 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 58 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 2.23 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 3.9 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 4.5 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 3.89 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 4.49 | % | ISO 294 |
| Kepadatan | 2.22 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.03 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 345 | °C |
| Suhu depan - Zona 3 | 360 - 370 | °C |
| Tengah - Zona 2 Suhu | 340 - 350 | °C |
| Bagian belakang - Zona 1 Suhu | 315 - 325 | °C |
| Suhu Cetakan | 140 - 165 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp 2X03624H.pdf |
|