SabikThermocompUF006Sresin adalah senyawa yang didasarkan pada resin Polyphthalamide yang mengandung Serat Kaca.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 196 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 2.4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 13560 | MPa | ASTM D 638 |
| Tekanan Flexural | 275 | MPa | ASTM D 790 |
| Modulus Flexural | 10210 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 726 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 85 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 258 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.28E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.22E-04 | 1/°C | ASTM E 831 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.43 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.2 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.2 - 0.4 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.5 - 0.7 | % | ASTM D 955 |
| Pakai faktor pencuci | 50 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Dimodifikasi |
| COF Dinamis | 0.48 | - | ASTM D 3702 Dimodifikasi |
| COF statis | 0.43 | - | ASTM D 3702 Dimodifikasi |
| Sumber GMD, terakhir diperbarui:12/17/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 | % |
| Suhu Peleburan | 315 - 330 | °C |
| Suhu depan - Zona 3 | 325 - 340 | °C |
| Tengah - Zona 2 Suhu | 315 - 325 | °C |
| Bagian belakang - Zona 1 Suhu | 310 - 320 | °C |
| Suhu Cetakan | 150 - 170 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:12/17/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
Untuk informasi lebih lanjut silahkan download lembar data | |
 | S-Plastics Thermocomp UF006S.pdf |
Dapatkan Kutipan Terbaru |