SabikThermocompQF006resin adalahsenyawa yang didasarkan pada resin Nylon 6/10 yang mengandung Serat Kaca.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 150 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 3.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 8410 | MPa | ASTM D 638 |
| Tekanan Flexural | 250 | MPa | ASTM D 790 |
| Modulus Flexural | 7860 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 153 | MPa | ISO 527 |
| Tekanan tarik, putus | 3.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 8800 | MPa | ISO 527 |
| Tekanan Flexural | 219 | MPa | ISO 178 |
| Modulus Flexural | 7800 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1116 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 122 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 9 | J | ASTM D 3763 |
| Dampak Multiaxial | 2 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 71 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 220 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 207 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 3.05E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.27E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 3.06E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.27E-05 | 1/°C | ISO 11359-2 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.309 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.2 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.2 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.17 - 0.18 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.98 - 0.99 | % | ISO 294 |
| Kepadatan | 1.3 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.33 | % | ISO 62 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94HB (3) | 1.5 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:10/02/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.12 - 0.2 | % |
| Suhu Peleburan | 270 - 275 | °C |
| Suhu depan - Zona 3 | 270 - 280 | °C |
| Tengah - Zona 2 Suhu | 260 - 270 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 260 | °C |
| Suhu Cetakan | 80 - 95 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/02/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp QF006.pdf |
|