SabikThermocompUC006Hresin adalah senyawa yang didasarkan pada resin Polyphthalamide yang mengandung Serat Karbon.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 287 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 26110 | MPa | ASTM D 638 |
| Tekanan Flexural | 419 | MPa | ASTM D 790 |
| Modulus Flexural | 22630 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 263 | MPa | ISO 527 |
| Tekanan tarik, putus | 1.3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 28160 | MPa | ISO 527 |
| Tekanan Flexural | 413 | MPa | ISO 178 |
| Modulus Flexural | 22320 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 827 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 74 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 8 | J | ASTM D 3763 |
| Dampak Multiaxial | 2 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 51 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 285 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 3.96E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 1.89E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 4.02E-05 | 1/°C | ISO 11359-2 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.324 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.31 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.2 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.6 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.16 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.62 | % | ISO 294 |
| Pakai faktor pencuci | 6 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Dimodifikasi |
| COF Dinamis | 0.27 | - | ASTM D 3702 Dimodifikasi |
| COF statis | 0.21 | - | ASTM D 3702 Dimodifikasi |
| Kepadatan | 1.32 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.66 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:10/02/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.15 | % |
| Suhu Peleburan | 315 - 330 | °C |
| Suhu depan - Zona 3 | 325 - 340 | °C |
| Tengah - Zona 2 Suhu | 315 - 325 | °C |
| Bagian belakang - Zona 1 Suhu | 310 - 320 | °C |
| Suhu Cetakan | 140 - 165 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/02/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |