SabikThermocompTH0450Aresin adalah senyawa yang didasarkan pada resin Polyurethane.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 20 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 19 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 40.9 | % | ASTM D 638 |
| Tekanan tarik, putus | 78.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 920 | MPa | ASTM D 638 |
| Tekanan Flexural | 18 | MPa | ASTM D 790 |
| Modulus Flexural | 660 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 18 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 18 | MPa | ISO 527 |
| Tekanan tarik, hasil | 26.6 | % | ISO 527 |
| Tekanan tarik, putus | 54.3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 850 | MPa | ISO 527 |
| Tekanan Flexural | 16 | MPa | ISO 178 |
| Modulus Flexural | 760 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | NB | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 432 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 22 | J | ASTM D 3763 |
| Dampak Multiaxial | 18 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 81 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 40 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 9.55E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 9.05E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 9.56E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 9.05E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 68 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 40 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 4.506 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.11 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 1 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.8 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 1.04 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.81 | % | ISO 294 |
| Kepadatan | 4.49 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.31 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.03 | % |
| Suhu Peleburan | 200 - 210 | °C |
| Suhu depan - Zona 3 | 195 - 205 | °C |
| Tengah - Zona 2 Suhu | 190 - 200 | °C |
| Bagian belakang - Zona 1 Suhu | 180 - 195 | °C |
| Suhu Cetakan | 15 - 45 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |