SabikThermocompTF006resin adalah LNP Thermocomp FF-1006 adalah serat kaca diisi Polyurethane.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 77 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 76 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 50 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 49 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 19.2 | % | ASTM D 638 |
| Tekanan tarik, putus | 21.5 | % | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 16.3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 16 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1480 | MPa | ASTM D 638 |
| Tekanan Flexural | 71 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 58 | MPa | ASTM D 790 |
| Modulus Flexural | 2060 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1690 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 69 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 69 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 51 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 51 | MPa | ISO 527 |
| Tekanan tarik, hasil | 13.7 | % | ISO 527 |
| Tekanan tarik, putus | 15.5 | % | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 15.5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 16 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1800 | MPa | ISO 527 |
| Tekanan Flexural | 66 | MPa | ISO 178 |
| Modulus Flexural | 2580 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2180 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | NB1751 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 512 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 19 | J | ASTM D 3763 |
| Dampak Multiaxial | 17 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 131 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 41 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 167 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 78 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.7E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.3E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 2.84E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.31E-04 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 167 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 85 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.47 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.36 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.1 - 0.4 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.5 - 0.8 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.15 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.4 | % | ISO 294 |
| Kepadatan | 1.47 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.5 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:10/02/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.03 | % |
| Suhu Peleburan | 210 - 215 | °C |
| Suhu depan - Zona 3 | 205 - 215 | °C |
| Tengah - Zona 2 Suhu | 200 - 210 | °C |
| Bagian belakang - Zona 1 Suhu | 190 - 200 | °C |
| Suhu Cetakan | 15 - 55 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/02/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp TF006.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|