SabikThermocompSF00Aresin adalah Kaca diisi Nylon 12
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 121 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 121 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 1.7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 12800 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 148 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 143 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 8930 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 113 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 113 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 1.5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 12280 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/menit | 10 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 577 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 97 | J/m | ASTM D 256 |
| Dampak Multiaxial | 16 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 30 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 1 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 176 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 166 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 176 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.48 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.2 - 0.4 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.8 - 1 | % | ASTM D 955 |
| Kepadatan | 1.48 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:02/07/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.12 - 0.2 | % |
| Suhu Peleburan | 225 - 240 | °C |
| Suhu depan - Zona 3 | 225 - 240 | °C |
| Tengah - Zona 2 Suhu | 220 - 230 | °C |
| Bagian belakang - Zona 1 Suhu | 215 - 225 | °C |
| Suhu Cetakan | 70 - 80 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:02/07/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |