SabikThermocompRX06324resin adalah Bahan ini mineral diisi kelas nilon dengan konstanta dielektrik tinggi
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 72 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 5120 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 120 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 120 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 4440 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 0 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 74 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 0 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 5230 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/menit | 5010 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 352 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 37 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 23 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 95 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 94 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 2.19 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 2 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 1.28 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1.08 | % | ASTM D 955 |
| Kepadatan | 2.19 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 270°C/1,2 kg | 17 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Faktor Dissipasi, 900MHz | 0.011 | - | ASTM D 150 |
| Permittivitas relatif, 900MHz | 7.9 | - | ASTM D 2520 - Mth B |
| Sumber GMD, terakhir diperbarui:2007/06/28 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 85 | °C |
| Waktu Pengeringan | 8 - 10 | jam |
| Suhu Peleburan | 260 - 270 | °C |
| Suhu Nozzle | 265 - 275 | °C |
| Suhu depan - Zona 3 | 265 - 270 | °C |
| Tengah - Zona 2 Suhu | 265 - 270 | °C |
| Bagian belakang - Zona 1 Suhu | 255 - 260 | °C |
| Suhu Cetakan | 90 | °C |
| Tekanan Belakang | 7 - 8 | MPa |
| Kecepatan sekrup | 110 - 130 | rpm |
| Sumber GMD, terakhir diperbarui:2007/06/28 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp RX06324.pdf |
|