SabikThermocompRX04515Hresin adalah senyawa yang didasarkan pada resin Nylon 66 yang mengandung Serat Karbon.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 286 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 286 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 2.5 | % | ASTM D 638 |
| Tekanan tarik, putus | 2.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 21230 | MPa | ASTM D 638 |
| Tekanan Flexural | 420 | MPa | ASTM D 790 |
| Modulus Flexural | 24060 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 971 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 80 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 255 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.32 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.1 - 0.3 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.5 - 0.7 | % | ASTM D 955 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 280 - 305 | °C |
| Suhu depan - Zona 3 | 295 - 305 | °C |
| Tengah - Zona 2 Suhu | 280 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 265 - 275 | °C |
| Suhu Cetakan | 95 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp RX04515H.pdf |
|