SabikThermocompPF005 resin adalah25% serat kaca diperkuat Polyamide 6 resin injeksi.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, pecah, 5 mm/menit | 150 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 3.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 7900 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 190 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 7800 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -20°C | 9 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -40°C | 7 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | 50 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 60°C, aliran | 3.1E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 9.1E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/120 | 222 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.2 - 0.3 | % | Metode S-Plastics |
| Kepadatan | 1.31 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 6.5 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+16 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+16 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 20 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 3.6 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 3.4 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.0061 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.016 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 500 | V | IEC 60112 |
| Indeks Pelacakan Perbandingan, M | 375 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94HB (3) | 0.75 | mm | UL 94 oleh GE |
| Glow Wire Flammability Index 650°C, melewati pada | 2 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 24 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:11/03/2003 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 75 - 85 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.2 | % |
| Suhu Peleburan | 250 - 280 | °C |
| Suhu Nozzle | 240 - 270 | °C |
| Suhu depan - Zona 3 | 250 - 280 | °C |
| Tengah - Zona 2 Suhu | 250 - 280 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 280 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 70 - 120 | °C |
| Sumber GMD, terakhir diperbarui:11/03/2003 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp PF005.pdf |
|