SabikThermocompOF002A resinadalah senyawa berbasis resin Polyphenylene Sulfide yang mengandung Serat Kaca.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 48 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 48 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 0.6 | % | ASTM D 638 |
| Tekanan tarik, putus | 0.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 8960 | MPa | ASTM D 638 |
| Tekanan Flexural | 82 | MPa | ASTM D 790 |
| Modulus Flexural | 6200 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 49 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 49 | MPa | ISO 527 |
| Tekanan tarik, hasil | 0.6 | % | ISO 527 |
| Tekanan tarik, putus | 0.6 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 7150 | MPa | ISO 527 |
| Tekanan Flexural | 98 | MPa | ISO 178 |
| Modulus Flexural | 6400 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 90 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 32 | J/m | ASTM D 256 |
| Dampak Multiaxial | 1 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 3 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 271 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 235 | °C | ASTM D 648 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 272 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 228 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.42 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.9 - 1.1 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.9 - 1.1 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 1 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 1 | % | ISO 294 |
| Kepadatan | 1.41 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 315 - 320 | °C |
| Suhu depan - Zona 3 | 330 - 345 | °C |
| Tengah - Zona 2 Suhu | 320 - 330 | °C |
| Bagian belakang - Zona 1 Suhu | 305 - 315 | °C |
| Suhu Cetakan | 140 - 165 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp OF002A.pdf |
|