SabikThermocompNX07354P resinadalah senyawa PC/ABS dengan kinerja plating yang lebih baik, kandidat yang baik untuk aplikasi Laser Direct Structuring.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 42 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 42 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 3.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 72.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2570 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 73 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 72 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2430 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 41 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 3.4 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 77.8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2520 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 75 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 74.2 | % | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2600 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 530 | J/m | ASTM D 256 |
| Izod Impact, bernotas 80*10*4 +23°C | 45 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 96 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 6.62E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.59E-05 | 1/°C | ASTM E 831 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 95 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.22 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.05 | % | ASTM D 570 |
| Penyusutan jamur, aliran (5) | 0.69 | % | Metode S-Plastics |
| Penyusutan jamur, xflow (5) | 0.61 | % | Metode S-Plastics |
| Kepadatan | 1.22 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Permittivitas relatif, 1 GHz | 2.8 | - | ASTM D 150 |
| Faktor Dissipasi, 1 GHz | 0.003 | - | ASTM D 150 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.5 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:2009/09/28 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 6 - 8 | jam |
| Suhu Peleburan | 235 - 255 | °C |
| Suhu Nozzle | 235 - 255 | °C |
| Suhu depan - Zona 3 | 235 - 255 | °C |
| Tengah - Zona 2 Suhu | 230 - 245 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 245 | °C |
| Suhu Cetakan | 60 - 80 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Sumber GMD, terakhir diperbarui:2009/09/28 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp NX07354P.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|