SabikThermocompNX07354 resinadalah senyawa PC/ABS, kandidat yang baik untuk aplikasi Laser Direct Structuring.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 53 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 43 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 42.3 | % | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 4.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2340 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 82 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 80 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2310 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 53 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 42 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 4.6 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 40 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2300 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 83 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 7.4 | % | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2240 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 606 | J/m | ASTM D 256 |
| Izod Impact, bernotas 80*10*4 +23°C | 54 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 106 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.55E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 8.48E-05 | 1/°C | ASTM E 831 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 105 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.23 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.2 | % | ASTM D 570 |
| Penyusutan jamur, aliran | 0.74 | % | Metode S-Plastics |
| Penyusutan jamur, aliran | 0.63 | % | Metode S-Plastics |
| Kepadatan | 1.23 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Permittivitas relatif, 1 GHz | 2.74 | - | ASTM D 150 |
| Faktor Dissipasi, 1 GHz | 0.003 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:2009/02/05 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 85 - 100 | °C |
| Waktu Pengeringan | 6 - 8 | jam |
| Suhu Peleburan | 240 - 280 | °C |
| Suhu Nozzle | 240 - 280 | °C |
| Suhu depan - Zona 3 | 240 - 270 | °C |
| Tengah - Zona 2 Suhu | 240 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 260 | °C |
| Suhu Cetakan | 60 - 100 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Sumber GMD, terakhir diperbarui:2009/02/05 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp NX07354.pdf |
|