SabikThermocompQC008resin adalahPA6.10, Serat Kaca,
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 233 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 233 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 1.8 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 44200 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 362 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 20270 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 237 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 237 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 1.6 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.6 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 31860 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/menit | 22440 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1344 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 127 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 68 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 11 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 222 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 217 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.94E+00 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 8.27E+00 | 1/°C | ASTM E 831 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 223 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 216 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.29 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.31 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 00.06 - 0.08 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.6 - 0.7 | % | ASTM D 955 |
| Kepadatan | 1.28 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.31 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:02/04/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.12 - 0.2 | % |
| Suhu Peleburan | 270 - 275 | °C |
| Suhu depan - Zona 3 | 270 - 280 | °C |
| Tengah - Zona 2 Suhu | 260 - 270 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 260 | °C |
| Suhu Cetakan | 80 - 95 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:02/04/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp QC008.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|