SabikThermocompPH0400BIresin adalahsenyawa yang didasarkan pada resin Nylon 6 yang mengandung High Specific Gravity Filler. Fitur tambahan dari bahan ini meliputi: High Specific Gravity, High Impact.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 35 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 35 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 1 | % | ASTM D 638 |
| Tekanan tarik, putus | 1.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 12960 | MPa | ASTM D 638 |
| Tekanan Flexural | 68 | MPa | ASTM D 790 |
| Modulus Flexural | 10290 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 260 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 58 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 15 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 150 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 4 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, xflow, 24 jam | 0.6 | % | ASTM D 955 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 265 - 270 | °C |
| Suhu depan - Zona 3 | 260 - 270 | °C |
| Tengah - Zona 2 Suhu | 250 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 250 | °C |
| Suhu Cetakan | 80 - 95 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp PH0400BI.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|