SabikThermocompMH0400A resinadalah senyawa yang didasarkan pada resin polipropilena.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 16 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 15 | MPa | ISO 527 |
| Tekanan tarik, hasil | 1.8 | % | ISO 527 |
| Tekanan tarik, putus | 2.6 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 6590 | MPa | ISO 527 |
| Tekanan Flexural | 36 | MPa | ISO 178 |
| Modulus Flexural | 9580 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Dampak Multiaxial | 2 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 91 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran, 24 jam | 0.89 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 1.01 | % | ISO 294 |
| Kepadatan | 4 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 210 - 225 | °C |
| Suhu depan - Zona 3 | 215 - 225 | °C |
| Tengah - Zona 2 Suhu | 205 - 215 | °C |
| Bagian belakang - Zona 1 Suhu | 195 - 205 | °C |
| Suhu Cetakan | 25 - 50 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp MH0400A.pdf |
|