SabikThermocompMFB63 resinadalah senyawa berbasis resin polipropilena yang mengandung Glass Bead, Glass Fiber.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 64 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 3.3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 5400 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 95 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 4900 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 60°C, aliran | 3.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 1.12E-04 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 154 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 133 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran (5) | 0.4 - 0.5 | % | Metode S-Plastics |
| Kepadatan | 1.22 | g/cm3 | ISO 1183 |
| Penyerapan air, 23°C/24 jam | 0.02 | % | ISO 62-1 |
| Sumber GMD, terakhir diperbarui:2010/08/17 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 225 - 250 | °C |
| Suhu depan - Zona 3 | 240 - 250 | °C |
| Tengah - Zona 2 Suhu | 215 - 225 | °C |
| Bagian belakang - Zona 1 Suhu | 195 - 205 | °C |
| Suhu Cetakan | 30 - 50 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:2010/08/17 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp MFB63.pdf |
|