SabikThermocompMF008S resinadalah senyawa berbasis resin polipropilena yang mengandung Serat Kaca.
Termasuk: Kemikalia.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 86 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 3 | % | ASTM D 638 |
| Tekanan Flexural | 137 | MPa | ASTM D 790 |
| Modulus Flexural | 7440 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 587 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 85 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 142 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.22 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.3 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1 | % | ASTM D 955 |
| Sumber GMD, terakhir diperbarui:10/02/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 225 - 250 | °C |
| Suhu depan - Zona 3 | 240 - 250 | °C |
| Tengah - Zona 2 Suhu | 215 - 225 | °C |
| Bagian belakang - Zona 1 Suhu | 195 - 205 | °C |
| Suhu Cetakan | 30 - 50 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/02/2004 | ||