SabikThermocompMF006SXP resin adalahsenyawa berbasis resin polipropilena yang mengandung Serat Kaca.
Termasuk: Kemikalia.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 88 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 7300 | MPa | ASTM D 638 |
| Tekanan Flexural | 139 | MPa | ASTM D 790 |
| Modulus Flexural | 6200 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 91 | MPa | ISO 527 |
| Tekanan tarik, putus | 3.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 7600 | MPa | ISO 527 |
| Tekanan Flexural | 159 | MPa | ISO 178 |
| Modulus Flexural | 8700 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 704 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 117 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 3 | J | ASTM D 3763 |
| Dampak Multiaxial | 2 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 45 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 11 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 160 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 150 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.64E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.97E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 2.64E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 5.98E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 152 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.134 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.02 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.5 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.5 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.96 | % | ISO 294 |
| Kepadatan | 1.13 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.03 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:10/02/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 225 - 250 | °C |
| Suhu depan - Zona 3 | 240 - 250 | °C |
| Tengah - Zona 2 Suhu | 215 - 225 | °C |
| Bagian belakang - Zona 1 Suhu | 195 - 205 | °C |
| Suhu Cetakan | 30 - 50 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/02/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp MF006SXP.pdf |
|